THE TEMPERATURE MEASUREMENTS OF POLYMETHYL METHACRYLATE UNDER SHOCK LOADING
The material was received by the Editorial Board: 15.11.2010
The brightness temperature was measured in polymethyl methacrylate shocked to 35 GPa by means of the fast two wavelengths optical pyrometer. The calibration of the pyrometer was performed by using a standard tungsten ribbon incandescent lamp prior to each shot. The measured brightness temperature at the wavelength λ = 550 nm was Tb = (1540 ± 30) K and at the wavelength λ = 630 nm it was Tb = (1510 ± 110) K. The results were compared with the temperature calculations obtained from different polymethyl methacrylate equations of state. The absorption coefficient of the shocked polymethyl methacrylate (α = 2.5 mm–1) was determined by using the time dependences in the pyrometric signals. Keywords:
polymethyl methacrylate, plexiglas, temperature, shock loading.
УДК 550.32
THE TEMPERATURE MEASUREMENTS OF POLYMETHYL METHACRYLATE UNDER SHOCK LOADING References: Bordzilovsky S. A., Karakhanov S. M. THE TEMPERATURE MEASUREMENTS OF POLYMETHYL METHACRYLATE UNDER SHOCK LOADING . Vestnik NSU. Series: Physics. 2011, vol. 6, no. 1. P. 116–122 (in Russ.). DOI: 10.54362/1818-7919-2011-6-1-116-122